Lms Fireproof and High Temperature Resistant Ceramic Silicone Fiberglass Fabric Sheet

• Certification: ISO, RoHS
• Application: Fireproof
• Surface Treatment: Silicon Coated
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: LMS-TSE
• Weave Type: Twill Woven
• Fiberglass Type: E-Glass
• Alkali Content: Medium
• Thickness: 0.2mm~1.0mm
• Width: 25mm~1200mm
• Density: 1.45~1.5g/Cm³
• Tensile Strength: 3.5MPa
• Volume Resistance: 1015.Cm
• Breakdown Voltage: 30kv/mm
• Smoke Toxicity: Za1
• Flammability Rating: V0
• Transport Package: Packing
• Specification: 0.6*1000*1000mm
• Trademark: LMS
• Origin: Guangdong
• HS Code: 3506919090
• Production Capacity: 5000 Pieces Per Day
• Package Size: 30.00cm * 20.00cm * 18.00cm
• Package Gross Weight: 10.000kg

Product Description

LMS Fireproof And High Temperature Resistant Ceramic Silicone Fiberglass Fabric Sheet

Product Description

Application

1.Replace mica tape.

2.Medium, high and low voltage fire-resistant and fire-resistant wires and cables.
3.Fireproof and fireproof protective cover for chemical cable.
4.Cable and cable accessories busbar or busbar coating. use.

Material data sheet

Test Item	Typical Vale	Unit	Standard
Density	1.45~1.5	g/cm³	ASTM D792
Tensile Strength	3.5	mpa	IEC 60811
Tear strength	20	KN/M	IEC 60811
Volume resistance	1015	.cm	IEC 60093
Breakdown voltage	30	kv/mm	IEC 60060
Smoke toxicity	ZA1	/	GB/T 20285
Flammability rating	V0	/	UL94
Water absorption	0.75	/	ASTM D570

 

Product description Application
Material: Fire-resistant silicone rubber and fire-resistant glass fiber cloth
Thickness::0.2mm~1.0mm
Width:25mm~1200mm.
Special size and packaging can be customized according to requirements

To wrap Lithium Battery to prevent Fire in case of Cathastrophic Failure.

Introduction
Laimesi ceramicized fire-resistant and fire-resistant composite tape is made of high-quality ceramicized fire-resistant and fire-resistant silicone rubber and fire-resistant glass fiber cloth after rolling and compounding, and then precision slitting.Under 450C or above high temperature or flame, it quickly hardens and forms a hard shell. This kind of shell plays a very good role in protecting the line or cable insulation, and is an environmentally friendly new material with comprehensive performance that replaces the traditional mica tape.
 

 

Feature
1. The ceramicized fire-resistant and fire-resistant composite tape can form a hard shell under high temperature or flame conditions of 450°C or above, ensuring that the line can still be unblocked in the event of a fire.
2. The ceramicized fire-resistant and refractory composite tape has good flexibility, can be wrapped and longitudinally wrapped, is simple and efficient to use, and can greatly reduce costs.
3. The ceramicized fireproof and refractory composite tape does not absorb moisture or water, and does not need to be pre-dried during use. The storage period is up to two years.
4. The ceramicized fireproof and refractory composite belt is low-smoke and halogen-free, does not contain sulfur, phosphorus, nitrogen, does not contain heavy metals, and does not melt. It is a non-toxic and harmless environmentally friendly new material.
5. The ceramicized fire-resistant and fire-resistant composite tape is used for wire and cable, which can be used as a fire-resistant layer and an insulating layer. The fire resistance level can reach the GB/T12666 Class A standard, and it can pass the CWZ water drench vibration fire resistance test of BS6387 Test.

LMS independent research and development products

 

Company Profile